    steel furniture often breaks at welds, where the metal was heated
    breifly to its melting temperature in order to join separate pieces together. why is the welded area of the steel harder and more prone to fracture than the rest of the steel ؟ سؤال للشطار


    0 Not allowed!

  2. #2
    عضو فعال

    User Info Menu

    i think i`ll get zero in this quiz


    0 Not allowed!
    [POEM="font="Simplified Arabic,4,darkblue,normal,normal" bkcolor="transparent" bkimage="" border="outset,7,black" type=2 line=0 align=center use=ex num="0,black""]النفس تبكى على الدنيا و قد علمت
    ان السلامه فيها ترك مافيها
    لا دار للمرء بعد الموت يسكنها
    الا التى كان قبل الموت يبنيها
    فمن بناها بخير طاب مسكنه
    ومن بناها بشر خاب بنيها[/POEM]

  3. #3

  4. #4
    عضو

    User Info Menu

    اجابة

    تعرف المنطقة المجاورة للدرزة اللحامية ( المنطقة المتأثرة بالحرارة )في هذخ المنطقة ونتيجة لمعدلات التسخين والتبريد يحصل نمو شديد في الحبيبات وهذا بدوره يؤدي لتناقص الخصائص الميكانيكية للدرزة اللحامية .
    ان الخصائص الفيزيائة والكيميائية للماده تتغير في موقع اللحام وفي المنطقة المتأثرة بالحرارة اثناء وبعد عملية اللحام على حد سواء هذه التغيرات تؤدي الى تغير في مقاومة الخضوع ومعامل المرونة.
    ايضا الاجهادات المتبقية والناتجة عن عمليات اللحام( اجهادات شد متبقبة ) لها اهمية كبيرة فأحيانا قد تصل الى مقدار يقارب حد الخضوع وهذا يسيء جدا للمادة.
    ايضا تحدث خلال وبعد عميليات اللحام تشققات ( باردة وساخنة ) تحدث بعد اللحام شقوق مايكروسكوبية تؤدي الى تناقص الخواص الميكانيكية . كما تلعب القصافة الهيدروجينو دورها في تناقص خواص الدرزة اللحامية.


    0 Not allowed!

  5. #5
    عضو

    User Info Menu

    جزالك الله خير اخي العزيز....ونفع الله بعلمك


    بس يريت لو كنت احصل على الجواب بالانجليزية


    0 Not allowed!

  6. #6
    عضو متميز

    User Info Menu

    Simplified

    Weld metal shrinks as it solidifies. Shrinkage causes stress
    Grain structure around the weld bead changes (Heat Affected Zone) See Picture
    Grain structure in (a) deep weld and (b) a shallow weld. Note that the grains in the solidified weld metal arc perpendicular to their interface with the base metal are perpendicular to their interface with the base metal. In a good weld, the solidification line at the center in the deep weld shown in (a) has grain migration, thus developing uniform strength in the weld bead

    So, when metal is overheated and cooled quickly it becomes hard and brittle. Metals have lower strength at high temperatures which will couse Weld metal to crack



    0 Not allowed!
    التعديل الأخير تم بواسطة weldit ; 2007-08-07 الساعة 08:18 AM

  7. #7
    عضو

    User Info Menu

    that's very kind of you
    thanks alot Mr weldit for explination


    0 Not allowed!

  8. #8
    عضو

    User Info Menu

    [GLOW="990033"]أخي الفضل ما معنى(breifly)[/GLOW]


    0 Not allowed!

  9. #9
    عضو

    User Info Menu

    لا بد من الاشارة إلى الاجهادة المتبقية في اللحام وبالقرب منه ويعود ذلك الى التقلص في معدن الدرزة وتبريده الى درجة الحرارة المحيطة ؟ وهنا المهم ان هذه الاجهادات يمكن ان تصل الى اجهاد الخضوع بالمقدار وتؤثر بطريقة مشابهة لتأثير الأحمال المركزة على السطح